describe the steps involved in a Dye penetrant inspection
|
The surface is Cleaned, and then Penetrant is applied & allowed to dwell for a specified time. Penetrant is then removed with an Emulsifier or Cleaner. once removed, the part is Dried and then Developer is applied. the results are then inspected and interpreted.
|
|
name some tools that are commonly used to assist in making visual inspections of welds
|
A magnifying glass, flashlight, mirror and, possibly a boroscope.
|
|
what are some of the nondestructive testing methods that may be used on aluminum parts
|
Visual, Dye penetrant, Eddy Current, Ultrasonic testing & radiography
|
|
What process occurs during the preparation stage of a dye penetrant inspection when the penetrating liquid is applied and then removed from a cracked part
|
The penetrant enters the crack by CApillary action and remains there until made visible by the developer.
|
|
A correctly made butt weld will have what Bead width and how much penetration?
|
The bead width should be 3 to 5 times the thickness of the base metal & there must be 100% penetration.
|
|
What telltale characteristic are evidence of a Cold weld
|
A cold weld has ROugh, Irregular edges that are not feathered into the base metal and has variations in penetration amounts.
|
|
The penetration of a fillet weld should be what percentage of the thickness of the base metal?
|
25 to 50 %
|
|
describe the basic steps for conducting a magnetic particle inspection
|
Magnetize the part, then COAT the surface with ferromagnetic particles. If a defect is present the particles align with the discontinuity forming a visible pattern
|